1. ZNP-54 ZINC PHOSPHATING CHEMICAL 2. Generally zinc phosphate conversion coating is used to provide long lasting corrosion protection. Almost all automotive industries use this type of conversion coating. It is suitable for the products come against hard weather conditions. Coating quality is better than iron phosphate coating. It forms 2 - 5 gr/m² coating on the metal surface when used as under paint. Application, set up and control of this process are more difficult than other methods and can be applied by immersion or spray. 3. Organic compounds like nickel and manganese are added to the bath to increase the coating performance. Also activation can be used to form small phosphate crystals on the metal surface before zinc phosphating. 4. Zinc phosphate reaction happens in amorphous shape with gray - black color. 5. pH optimizers are added to accelerate the reaction. Temperature, application time, concentration, pH, total acid and free acid values are the parameters which must be under control. 6. Zinc phosphates, coating range between 7 - 15 gr/m², are used in wire drawing, tube drawing and cold forming industries. Phosphated metal workpieces are prepared to the next stage by application of protective lubricans and soap

PASSIVATION - PSV-72 - INTRODUCTION & APPLICATION : - PASSIVATION is a cold & hot Passivation Solution used in the final rinse after - Phosphating. In hot Passivation temperature 700c. - BATH MAKE-UP : - Passivation Solution make by 0.1% v/v. Rinse the phosphate material dip in - passivation bath 1 minute. - BATH MAINTENANCE : - Passivation should be clean. if bath is contaminating it should be discard & make - up new bath.

VC AR306 INTRODUCTION : VC AR306 is a powder based activator which is used at low concentrations prior to zinc phosphating. By dipping the parts in VC AR306 bath prior to phosphating, it accelerates the subsequent phosphating process and also refines the structure of the zinc phosphate coating resulting in smooth fine uniform compact coating. PROPERTIES : Colour : White Form : Free flowing powder PH of 0.2-0.3% : 8-9 APPLICATION : VC AR306 bath can be prepared in M.S. or plastic tank/container. It is to be used at 0.2% to 0.3% concentration with water, at room temperature for one minute. The bath should always be kept in a slightly agitated condition by mechanical means or by passing compressed air from the bottom of the tank to avoid settling of the activator at the bottom of the tank. MAINTENANCE OF BATH : Once the bath is prepared, daily addition should be made once during the day. Addition should be made when pH falls below 8. Always maintain pH between 8-9. New bath should be prepared once in week or once in 15 days, depending on the work load. PRECAUTION : 1. Since the product is alkaline in nature always wear PVC/Rubber gloves while handling or working with this product. 2. Any splashes on skin or eyes should be flushed off with plenty of water and thereafter immediately consult physician. 3. Use of eye goggles and apron is recommended. PACKING : 15 Kgs & 50 Kgs.

COROLITE 9 chemical In line with clients diverse requirements, we are involved in providing an optimum quality range of COROLITE 9 chemical Also use as Anti corrosive solutions COROLITE 9 chemical is a solution which together does the work of:- Degreasing- removing oil, grease, dirt etc. Derusting- removes rust, scales etc Phosphating- provides a very light layer of iron phosphate.

ZNP-54 ZINC PHOSPHATING CHEMICAL Generally zinc phosphate conversion coating is used to provide long lasting corrosion protection. Almost all automotive industries use this type of conversion coating. It is suitable for the products come against hard weather conditions. Coating quality is better than iron phosphate coating. It forms 2 - 5 gr/m coating on the metal surface when used as under paint. Application, set up and control of this process are more difficult than other methods and can be applied by immersion or spray. Organic compounds like nickel and manganese are added to the bath to increase the coating performance. Also activation can be used to form small phosphate crystals on the metal surface before zinc phosphating. Zinc phosphate reaction happens in amorphous shape with gray - black color. pH optimizers are added to accelerate the reaction. Temperature, application time, concentration, pH, total acid and free acid values are the parameters which must be under control. Zinc phosphates, coating range between 7 - 15 gr/m, are used in wire drawing, tube drawing and cold forming industries. Phosphated metal workpieces are prepared to the next stage by application of protective lubricans and soap

Vitarag Chemicals welcomes you. We are proud to introduce ourselves as the leading manufacturer, suppliers of metal pretreatment chemicals in India. PCR 01 paint remover solutions is heavy duty industrial Powder coating remover used for removal of paint & powder coating from the metal surface. The chemical penetrates through the film and the film bubbles out. It is used to remove all types of liquid as well as powder paints, lacquers, enamels & polyurethanes from a metal surface. PCR 01 paint remover solutions is used by immersion application at room temperature. The dipping time may range from 1 to 5 min depending on the surrounding temperature, nature, and thickness of the paint. It may also be applied by brush on the surface of the coating to be removed. Allow standing for 1 to 5 min, depending on the nature and thickness of the coating to be removed. Two or more brush may have to be applied for complete removal of stubborn paint. Remove by scraping, brushing or water jet application. While there are several reasons why you should go for our company: We formulate products based on the end users specific requirements through extensive R& D and validation procedures. We provide reliable and quality products timely as we maintain strict quality control procedures for our raw materials and finished goods. We offer comprehensive customer support post supply We supply products at most competitive prices.In line with clients diverse requirements, we are involved in providing an optimum quality range of Powder Coating /Paint Remover Chemical.

Industrial Blackening Solutions is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature. VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energy saving, fast, dependable and convenient. It increases productivity and lowers labour costs. Finishing can be done anywhere without special equipment, ventilation, heating systems or any complicated control procedures. EQUIPMENT REQUIRED Acid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used with VCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks and racks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used for degreasing, rinsing & sealant tanks. DIRECTIONS FOR USE 1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree of surface soil will determine the length of time and the number of cleaning steps and cleaning temperature (M.S. Tank). 2. Rinse thoroughly in overflowing cold water (M.S. Tank). 3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at a concentration of 1:1 at room temperature (FRP Tank). 4. Rinse thoroughly in overflowing cold water (M.S. Tank). 5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6 to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary to produce the desired depth of black, is usually one to three minutes. For most parts a dilution of one part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank). 6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank).

INTRODUCTION: Degreasing Chemical used whenever parts contains heavy grease, oil & light rust. This chemical also removes certain part of carbon. Base : Alkaline Base Chemical. Solubility : Thoroughly soluble in water. Color : white Concentration : 5% (w/v) is suitable for Hot process & in case of cold 8% required. Point : Concentrated of 8% bath Solution gives 6 to 8 ml. Point. Bath Design : Tank is made up of 10mm thick. M.S. tank with F.R.P. Vinyl coat of F.R.P. Lining works will be the most suitable or sustainable design

Base : Phosphoric Acid Base Chemical.Solubility : Thoroughly soluble in water.Color : Water White.Concentration : One part of chemical is diluted with two to four parts of water DilutionIs depended by the amount of oil present. The chemical is used cold.Point : Concentrated of 25 % bath solution gives 8 to 10 ml.Application : This chemical is used whenever parts contain light grease and OIL.