Vitarag Chemicals welcomes you. We are proud to introduce ourselves as the leading manufacturer, suppliers of metal pretreatment chemicals in India. PCR 01 paint remover solutions is heavy duty industrial Powder coating remover used for removal of paint & powder coating from the metal surface. The chemical penetrates through the film and the film bubbles out. It is used to remove all types of liquid as well as powder paints, lacquers, enamels & polyurethanes from a metal surface. PCR 01 paint remover solutions is used by immersion application at room temperature. The dipping time may range from 1 to 5 min depending on the surrounding temperature, nature, and thickness of the paint. It may also be applied by brush on the surface of the coating to be removed. Allow standing for 1 to 5 min, depending on the nature and thickness of the coating to be removed. Two or more brush may have to be applied for complete removal of stubborn paint. Remove by scraping, brushing or water jet application. While there are several reasons why you should go for our company: We formulate products based on the end users specific requirements through extensive R& D and validation procedures. We provide reliable and quality products timely as we maintain strict quality control procedures for our raw materials and finished goods. We offer comprehensive customer support post supply We supply products at most competitive prices.In line with clients diverse requirements, we are involved in providing an optimum quality range of Powder Coating /Paint Remover Chemical.

Industrial Blackening Solutions is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature. VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energy saving, fast, dependable and convenient. It increases productivity and lowers labour costs. Finishing can be done anywhere without special equipment, ventilation, heating systems or any complicated control procedures. EQUIPMENT REQUIRED Acid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used with VCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks and racks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used for degreasing, rinsing & sealant tanks. DIRECTIONS FOR USE 1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree of surface soil will determine the length of time and the number of cleaning steps and cleaning temperature (M.S. Tank). 2. Rinse thoroughly in overflowing cold water (M.S. Tank). 3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at a concentration of 1:1 at room temperature (FRP Tank). 4. Rinse thoroughly in overflowing cold water (M.S. Tank). 5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6 to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary to produce the desired depth of black, is usually one to three minutes. For most parts a dilution of one part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank). 6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank).

INTRODUCTION: Degreasing Chemical used whenever parts contains heavy grease, oil & light rust. This chemical also removes certain part of carbon. Base : Alkaline Base Chemical. Solubility : Thoroughly soluble in water. Color : white Concentration : 5% (w/v) is suitable for Hot process & in case of cold 8% required. Point : Concentrated of 8% bath Solution gives 6 to 8 ml. Point. Bath Design : Tank is made up of 10mm thick. M.S. tank with F.R.P. Vinyl coat of F.R.P. Lining works will be the most suitable or sustainable design

Base : Phosphoric Acid Base Chemical.Solubility : Thoroughly soluble in water.Color : Water White.Concentration : One part of chemical is diluted with two to four parts of water DilutionIs depended by the amount of oil present. The chemical is used cold.Point : Concentrated of 25 % bath solution gives 8 to 10 ml.Application : This chemical is used whenever parts contain light grease and OIL.

CHROMATIZING Aluminium chromate and its applications What we call as phosphating to steel an iron is called chromating for aluminium surfaces. Also it is knows as alodine coating. There are yellow, green and transparent chromating types. Yellow chromate coats Cr+6, green chromate coats Cr+3. Coating weight can vary according to application time and coating type. Drying temperature must not pass over 65 º C for yellow chromate and 85 º C for green and transparent chromate coatings. It is importat to provide clean, grease free surface before chromate application. If hot degreasing bath is prepared, caustic bath and following nitric acid bath can be used for pickling. On the other hand, acidic degreasing baths have pickling ability with itselves. Chromating and paint adhesion will be much better on pickled and degreased aluminium surface.

We deal in Room Temperature blackening Chemical, which customer can directly avail from us. GENERAL DESCRIPTION VCBLK HB-18 is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature.VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energysaving, fast, dependable and convenient. It increases productivity and lowers labour costs.Finishing can be done anywhere without special equipment, ventilation, heating systems or anycomplicated control procedures.EQUIPMENT REQUIREDAcid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used withVCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks andracks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used fordegreasing, rinsing & sealant tanks.DIRECTIONS FOR USE1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree ofsurface soil will determine the length of time and the number of cleaning steps and cleaningtemperature (M.S. Tank).2. Rinse thoroughly in overflowing cold water (M.S. Tank).3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at aconcentration of 1:1 at room temperature (FRP Tank).4. Rinse thoroughly in overflowing cold water (M.S. Tank).5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary toproduce the desired depth of black, is usually one to three minutes. For most parts a dilution ofone part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank).6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank). 7. Immerse the pieces in oil, a dewatering type rust preventive at room temperature for 3 minutesto seal the finish and impart corrosion resistance (M.S. Tank).The above parts can be sealed while wet or dry. If parts have to be dried prior to sealing, step 6should be followed with a hot water rinse and the parts to be sealed as soon as they are dry.A wide range of rust preventives are available with us. Consult us on what type of finish andprotection you require for your parts or components and we can suggest a suitable oil.

We deal in Room Temperature blackening Chemical, which customer can directly avail from us. GENERAL DESCRIPTION VCBLK HB-18 is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature.VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energysaving, fast, dependable and convenient. It increases productivity and lowers labour costs.Finishing can be done anywhere without special equipment, ventilation, heating systems or anycomplicated control procedures.EQUIPMENT REQUIREDAcid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used withVCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks andracks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used fordegreasing, rinsing & sealant tanks.DIRECTIONS FOR USE1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree ofsurface soil will determine the length of time and the number of cleaning steps and cleaningtemperature (M.S. Tank).2. Rinse thoroughly in overflowing cold water (M.S. Tank).3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at aconcentration of 1:1 at room temperature (FRP Tank).4. Rinse thoroughly in overflowing cold water (M.S. Tank).5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary toproduce the desired depth of black, is usually one to three minutes. For most parts a dilution ofone part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank).6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank). 7. Immerse the pieces in oil, a dewatering type rust preventive at room temperature for 3 minutesto seal the finish and impart corrosion resistance (M.S. Tank).The above parts can be sealed while wet or dry. If parts have to be dried prior to sealing, step 6should be followed with a hot water rinse and the parts to be sealed as soon as they are dry.A wide range of rust preventives are available with us. Consult us on what type of finish andprotection you require for your parts or components and we can suggest a suitable oil.

Base : Phosphoric Acid Base Chemical. Solubility : Thoroughly soluble in water. Color : Water White. Concentration : One part of chemical is diluted with two to four parts of water. Dilution Is depended by the amount of oil present. The chemical is used cold. Point : Concentrated of 25 % bath solution gives 8 to 10 ml. Application : This chemical is used whenever parts contain light grease and OIL.

TMT BAR RUST REMOVER Derusting chemical removes rust & carbon from metal & cleans metal surface. Ensure that oxide scales & rust formation is removed. This chemical used whenever parts contains heavy rust and light oil. Base : Phosphoric Acid Base Chemical. Solubility : Thoroughly soluble in water. Color : Colourless . Concentration : One part of chemical is diluted with three parts of water. Dilution depends by the amount of rust present. The chemical is used cold. Point : Concentrated of 25 % bath Solution gives 20 to 22 ml. Point. Bath Design : Tank is made up of 10mm thick. M.S. tank with F.R.P. Vinyl coat of F.R.P. Lining works will be the most suitable or sustainable design of tank. Packing : 40 Kgs. In PVC container Yield Frequency : 250 - 300 Sq. Ft. per liter.