We deal in Room Temperature blackening Chemical, which customer can directly avail from us. GENERAL DESCRIPTION VCBLK HB-18 is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature.VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energysaving, fast, dependable and convenient. It increases productivity and lowers labour costs.Finishing can be done anywhere without special equipment, ventilation, heating systems or anycomplicated control procedures.EQUIPMENT REQUIREDAcid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used withVCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks andracks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used fordegreasing, rinsing & sealant tanks.DIRECTIONS FOR USE1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree ofsurface soil will determine the length of time and the number of cleaning steps and cleaningtemperature (M.S. Tank).2. Rinse thoroughly in overflowing cold water (M.S. Tank).3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at aconcentration of 1:1 at room temperature (FRP Tank).4. Rinse thoroughly in overflowing cold water (M.S. Tank).5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary toproduce the desired depth of black, is usually one to three minutes. For most parts a dilution ofone part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank).6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank). 7. Immerse the pieces in oil, a dewatering type rust preventive at room temperature for 3 minutesto seal the finish and impart corrosion resistance (M.S. Tank).The above parts can be sealed while wet or dry. If parts have to be dried prior to sealing, step 6should be followed with a hot water rinse and the parts to be sealed as soon as they are dry.A wide range of rust preventives are available with us. Consult us on what type of finish andprotection you require for your parts or components and we can suggest a suitable oil.

We deal in Room Temperature blackening Chemical, which customer can directly avail from us. GENERAL DESCRIPTION VCBLK HB-18 is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature.VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energysaving, fast, dependable and convenient. It increases productivity and lowers labour costs.Finishing can be done anywhere without special equipment, ventilation, heating systems or anycomplicated control procedures.EQUIPMENT REQUIREDAcid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used withVCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks andracks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used fordegreasing, rinsing & sealant tanks.DIRECTIONS FOR USE1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree ofsurface soil will determine the length of time and the number of cleaning steps and cleaningtemperature (M.S. Tank).2. Rinse thoroughly in overflowing cold water (M.S. Tank).3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at aconcentration of 1:1 at room temperature (FRP Tank).4. Rinse thoroughly in overflowing cold water (M.S. Tank).5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary toproduce the desired depth of black, is usually one to three minutes. For most parts a dilution ofone part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank).6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank). 7. Immerse the pieces in oil, a dewatering type rust preventive at room temperature for 3 minutesto seal the finish and impart corrosion resistance (M.S. Tank).The above parts can be sealed while wet or dry. If parts have to be dried prior to sealing, step 6should be followed with a hot water rinse and the parts to be sealed as soon as they are dry.A wide range of rust preventives are available with us. Consult us on what type of finish andprotection you require for your parts or components and we can suggest a suitable oil.

VC AR306 INTRODUCTION : VC AR306 is a powder based activator which is used at low concentrations prior to zinc phosphating. By dipping the parts in VC AR306 bath prior to phosphating, it accelerates the subsequent phosphating process and also refines the structure of the zinc phosphate coating resulting in smooth fine uniform compact coating. PROPERTIES : Colour : White Form : Free flowing powder PH of 0.2-0.3% : 8-9 APPLICATION : VC AR306 bath can be prepared in M.S. or plastic tank/container. It is to be used at 0.2% to 0.3% concentration with water, at room temperature for one minute. The bath should always be kept in a slightly agitated condition by mechanical means or by passing compressed air from the bottom of the tank to avoid settling of the activator at the bottom of the tank. MAINTENANCE OF BATH : Once the bath is prepared, daily addition should be made once during the day. Addition should be made when pH falls below 8. Always maintain pH between 8-9. New bath should be prepared once in week or once in 15 days, depending on the work load. PRECAUTION : 1. Since the product is alkaline in nature always wear PVC/Rubber gloves while handling or working with this product. 2. Any splashes on skin or eyes should be flushed off with plenty of water and thereafter immediately consult physician. 3. Use of eye goggles and apron is recommended. PACKING : 15 Kgs & 50 Kgs.

SURGICAL INSTRUMENT RUST REMOVER Surgical instrument Rust Remover is a powerful rust dis-integrating solution. It is a quality product that has been a trusted for Rust removing for years. This is a multipurpose maintenance aid and significantly reduces the maintenance cost. It is specially formulated to fight rust, which makes it indispensable to industrial plant, factories and garages. Overall Surgical instriment Rust Remover acts as a dis-integrator, dismantler, Lubricator, decarboniser & cleaner The active ingredients in Surgical instriment Rust Remover attack the point where rust and metal parts are bound together and consequently eliminate rust from the surface. It also penetrates the tightest of joints reaches between the finest of threads and enters the innermost points of inaccessible mechanisms Non Messy Non Injurious Saves Time & Labour Excellent film spreading properly Excellent penetrating properties Non Corrosives

We deal in Room Temperature blackening Chemical, which customer can directly avail from us. GENERAL DESCRIPTION VCBLK HB-18 is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature.VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energysaving, fast, dependable and convenient. It increases productivity and lowers labour costs.Finishing can be done anywhere without special equipment, ventilation, heating systems or anycomplicated control procedures.EQUIPMENT REQUIREDAcid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used withVCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks andracks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used fordegreasing, rinsing & sealant tanks.DIRECTIONS FOR USE1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree ofsurface soil will determine the length of time and the number of cleaning steps and cleaningtemperature (M.S. Tank).2. Rinse thoroughly in overflowing cold water (M.S. Tank).3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at aconcentration of 1:1 at room temperature (FRP Tank).4. Rinse thoroughly in overflowing cold water (M.S. Tank).5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary toproduce the desired depth of black, is usually one to three minutes. For most parts a dilution ofone part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank).6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank). 7. Immerse the pieces in oil, a dewatering type rust preventive at room temperature for 3 minutesto seal the finish and impart corrosion resistance (M.S. Tank).The above parts can be sealed while wet or dry. If parts have to be dried prior to sealing, step 6should be followed with a hot water rinse and the parts to be sealed as soon as they are dry.A wide range of rust preventives are available with us. Consult us on what type of finish andprotection you require for your parts or components and we can suggest a suitable oil.

Vitarag Chemicals is a leading manufacturer of metal Pre Treatment Chemicals which can also be known as powder coating chemicals manufacturer. We have been manufacturing and supplying pre treatment chemicals to High-Temperature Resistant Powder Coating Chemicals in India and out of India.

We deal in Room Temperature blackening Chemical, which customer can directly avail from us. GENERAL DESCRIPTION VCBLK HB-18 is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature.VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energysaving, fast, dependable and convenient. It increases productivity and lowers labour costs.Finishing can be done anywhere without special equipment, ventilation, heating systems or anycomplicated control procedures.EQUIPMENT REQUIREDAcid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used withVCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks andracks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used fordegreasing, rinsing & sealant tanks.DIRECTIONS FOR USE1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree ofsurface soil will determine the length of time and the number of cleaning steps and cleaningtemperature (M.S. Tank).2. Rinse thoroughly in overflowing cold water (M.S. Tank).3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at aconcentration of 1:1 at room temperature (FRP Tank).4. Rinse thoroughly in overflowing cold water (M.S. Tank).5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary toproduce the desired depth of black, is usually one to three minutes. For most parts a dilution ofone part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank).6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank). 7. Immerse the pieces in oil, a dewatering type rust preventive at room temperature for 3 minutesto seal the finish and impart corrosion resistance (M.S. Tank).The above parts can be sealed while wet or dry. If parts have to be dried prior to sealing, step 6should be followed with a hot water rinse and the parts to be sealed as soon as they are dry.A wide range of rust preventives are available with us. Consult us on what type of finish andprotection you require for your parts or components and we can suggest a suitable oil.

1. ZNP-54 ZINC PHOSPHATING CHEMICAL 2. Generally zinc phosphate conversion coating is used to provide long lasting corrosion protection. Almost all automotive industries use this type of conversion coating. It is suitable for the products come against hard weather conditions. Coating quality is better than iron phosphate coating. It forms 2 - 5 gr/m² coating on the metal surface when used as under paint. Application, set up and control of this process are more difficult than other methods and can be applied by immersion or spray. 3. Organic compounds like nickel and manganese are added to the bath to increase the coating performance. Also activation can be used to form small phosphate crystals on the metal surface before zinc phosphating. 4. Zinc phosphate reaction happens in amorphous shape with gray - black color. 5. pH optimizers are added to accelerate the reaction. Temperature, application time, concentration, pH, total acid and free acid values are the parameters which must be under control. 6. Zinc phosphates, coating range between 7 - 15 gr/m², are used in wire drawing, tube drawing and cold forming industries. Phosphated metal workpieces are prepared to the next stage by application of protective lubricans and soap

CHROMATIZING Aluminium chromate and its applications What we call as phosphating to steel an iron is called chromating for aluminium surfaces. Also it is knows as alodine coating. There are yellow, green and transparent chromating types. Yellow chromate coats Cr+6, green chromate coats Cr+3. Coating weight can vary according to application time and coating type. Drying temperature must not pass over 65 º C for yellow chromate and 85 º C for green and transparent chromate coatings. It is importat to provide clean, grease free surface before chromate application. If hot degreasing bath is prepared, caustic bath and following nitric acid bath can be used for pickling. On the other hand, acidic degreasing baths have pickling ability with itselves. Chromating and paint adhesion will be much better on pickled and degreased aluminium surface.