Vitarag Chemicals is a leading manufacturer of metal Pre Treatment Chemicals which can also be known as powder coating chemicals manufacturer. We have been manufacturing and supplying pre treatment chemicals to Powder Coating Chemicals For Metal Surfaces in India and out of India.

RLN 27 Derusting Rust Remover Chemical RLN 27 Derusting Rust Remover Chemical dissolves rust quickly without harming surrounding parts, trim, gaskets or paint. Our rust remover restores surfaces to bare metal without scraping, chipping or scrubbing. To remove light rust, leave the parts in remove heavy rust, leave parts in the rust removal solution 30 min This non-toxic and biodegradable rust remover formula is effective on small or large items that can be RLN 27 Derusting rln-27 rust remover dissolves rust quickly without harming surrounding parts, trim, gaskets or paint. our rust remover restores surfaces to bare metal without scraping, chipping or scrubbing. to remove light rust, leave the parts in 10-20 min and to remove heavy rust, leave parts in the rust removal solution 30 min.this non-toxic and biodegradable rust remover formula is effective on small or large items that can be soaked. with our expertise and trustworthiness, we are engaged in offering an optimum quality range of RLN 27 Derusting chemical. RLN 27 Derusting chemical is used for removing rust, scales, welding scales, thin film of oil and grease. this chemical has replaced the use of hydrochloric acid for rust removal. we make sure that this chemical is formulated using environmentally safe acids.

Blackening Products For Metal Surfaces is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature. VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energy saving, fast, dependable and convenient. It increases productivity and lowers labour costs. Finishing can be done anywhere without special equipment, ventilation, heating systems or any complicated control procedures. EQUIPMENT REQUIRED Acid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used with VCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks and racks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used for degreasing, rinsing & sealant tanks. DIRECTIONS FOR USE 1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree of surface soil will determine the length of time and the number of cleaning steps and cleaning temperature (M.S. Tank). 2. Rinse thoroughly in overflowing cold water (M.S. Tank). 3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at a concentration of 1:1 at room temperature (FRP Tank). 4. Rinse thoroughly in overflowing cold water (M.S. Tank). 5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6 to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary to produce the desired depth of black, is usually one to three minutes. For most parts a dilution of one part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank). 6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank).

Blackening Chemicals For Metalworking is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature. VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energy saving, fast, dependable and convenient. It increases productivity and lowers labour costs. Finishing can be done anywhere without special equipment, ventilation, heating systems or any complicated control procedures. EQUIPMENT REQUIRED Acid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used with VCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks and racks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used for degreasing, rinsing & sealant tanks. DIRECTIONS FOR USE 1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree of surface soil will determine the length of time and the number of cleaning steps and cleaning temperature (M.S. Tank). 2. Rinse thoroughly in overflowing cold water (M.S. Tank). 3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at a concentration of 1:1 at room temperature (FRP Tank). 4. Rinse thoroughly in overflowing cold water (M.S. Tank). 5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6 to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary to produce the desired depth of black, is usually one to three minutes. For most parts a dilution of one part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank). 6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank).

Blackening Chemicals For Sale is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature. VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energy saving, fast, dependable and convenient. It increases productivity and lowers labour costs. Finishing can be done anywhere without special equipment, ventilation, heating systems or any complicated control procedures. EQUIPMENT REQUIRED Acid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used with VCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks and racks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used for degreasing, rinsing & sealant tanks. DIRECTIONS FOR USE 1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree of surface soil will determine the length of time and the number of cleaning steps and cleaning temperature (M.S. Tank). 2. Rinse thoroughly in overflowing cold water (M.S. Tank). 3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at a concentration of 1:1 at room temperature (FRP Tank). 4. Rinse thoroughly in overflowing cold water (M.S. Tank). 5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6 to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary to produce the desired depth of black, is usually one to three minutes. For most parts a dilution of one part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank). 6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank).

Blackening Chemicals For Manufacturing Industry is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature. VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energy saving, fast, dependable and convenient. It increases productivity and lowers labour costs. Finishing can be done anywhere without special equipment, ventilation, heating systems or any complicated control procedures. EQUIPMENT REQUIRED Acid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used with VCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks and racks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used for degreasing, rinsing & sealant tanks. DIRECTIONS FOR USE 1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree of surface soil will determine the length of time and the number of cleaning steps and cleaning temperature (M.S. Tank). 2. Rinse thoroughly in overflowing cold water (M.S. Tank). 3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at a concentration of 1:1 at room temperature (FRP Tank). 4. Rinse thoroughly in overflowing cold water (M.S. Tank). 5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6 to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary to produce the desired depth of black, is usually one to three minutes. For most parts a dilution of one part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank). 6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank).

Blackening Chemicals For Automotive Industry is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature. VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energy saving, fast, dependable and convenient. It increases productivity and lowers labour costs. Finishing can be done anywhere without special equipment, ventilation, heating systems or any complicated control procedures. EQUIPMENT REQUIRED Acid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used with VCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks and racks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used for degreasing, rinsing & sealant tanks. DIRECTIONS FOR USE 1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree of surface soil will determine the length of time and the number of cleaning steps and cleaning temperature (M.S. Tank). 2. Rinse thoroughly in overflowing cold water (M.S. Tank). 3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at a concentration of 1:1 at room temperature (FRP Tank). 4. Rinse thoroughly in overflowing cold water (M.S. Tank). 5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6 to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary to produce the desired depth of black, is usually one to three minutes. For most parts a dilution of one part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank). 6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank).

Powder Coating Chemicals for Industrial Communication 7-Tank Process Chemicals for Powder-Coating : A Comprehensive GuideDiscover the top-quality chemicals from Vitarag Chemicals for the 8-tank process. Our specially made formulas are perfect for modern industries, giving you great performance and reliability. Improve your work with our latest products, made by experts with lots of experience. When you’re powder coating, it’s very much necessary to use good chemicals for a perfect finish.Vitarag Chemicals has the right products for each step of the powder coating process. Start with our cleaners, which remove dirt and grease from metal surfaces. They also help you in making them ready for painting. Then use our special phosphating chemicals to protect the metal from rust and help the paint stick better. With Vitarag Chemicals, you get top-notch quality and expertise. Our chemicals make the powder coating process superior, giving you professional-looking finishes that meet all the standards. Each chemical in the eight-tank process is important, helping you get great results every time.

DESCRIPTION : VCCLEAN-550 is a very effective deburring compound. It can also be used for cleaning, degreasing, derusting, descaling etc. when used in tumblers, vibrators, agitators and deburring equipments. It will remove all loose deposits producing a very smooth and even surface on the components. It can very safely be used for ferrous as well as non-ferrous metals. It is non-toxic and very safe to handle. USES : 1. For deburring ferrous & non-ferrous components. 2. For removal of rust & scales from components when used in tumblers & vibrators etc. alongwith some suitable media APPLICATION :- 1. Add 5-10% of VCCLEAN-550 based on the water added to the tank of the vibrator/tumbler etc. 2. Operate the equipment for a time ranging from ½ hr – 6 hrs depending on the type of operation. Regular addition of chemical may have ro be made for long duration of operation 3. Rinse tumble the components with fresh water. 4. Dip them in a suitable rust preventive like RUST PREVENTIVE OIL depending on the desired period of protection.