GENERAL DESCRIPTION. VCBLK HB-18 is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature.VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energysaving, fast, dependable and convenient. It increases productivity and lowers labour costs.Finishing can be done anywhere without special equipment, ventilation, heating systems or anycomplicated control procedures.EQUIPMENT REQUIREDAcid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used withVCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks andracks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used fordegreasing, rinsing & sealant tanks.DIRECTIONS FOR USE1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree ofsurface soil will determine the length of time and the number of cleaning steps and cleaningtemperature (M.S. Tank).2. Rinse thoroughly in overflowing cold water (M.S. Tank).3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at aconcentration of 1:1 at room temperature (FRP Tank).4. Rinse thoroughly in overflowing cold water (M.S. Tank).5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary toproduce the desired depth of black, is usually one to three minutes. For most parts a dilution ofone part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank).6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank). 7. Immerse the pieces in oil, a dewatering type rust preventive at room temperature for 3 minutesto seal the finish and impart corrosion resistance (M.S. Tank).The above parts can be sealed while wet or dry. If parts have to be dried prior to sealing, step 6should be followed with a hot water rinse and the parts to be sealed as soon as they are dry.A wide range of rust preventives are available with us. Consult us on what type of finish andprotection you require for your parts or components and we can suggest a suitable oil.

ALKALINE STRIPPER 108 is a specially formulated alkaline composition containing sequestrants andsurface active agents. It is recommended for use on ferrous components for removal of various soils,greases oils, lubricants, drawing & stamping compounds, paints, varnishes and carbon deposits. It alsoremoves light to medium rust from ferrous metal surfaces very effectively. Due to its versatile cleaningproperties, it is widely used for a variety of cleaning applications. ALKALINE STRIPPER 108 shouldnot be used on non-ferrous components. It is non-toxic but corrosive to skin.

We deal in Room Temperature blackening Chemical, which customer can directly avail from us. GENERAL DESCRIPTION VCBLK HB-18 is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature.VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energysaving, fast, dependable and convenient. It increases productivity and lowers labour costs.Finishing can be done anywhere without special equipment, ventilation, heating systems or anycomplicated control procedures.EQUIPMENT REQUIREDAcid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used withVCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks andracks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used fordegreasing, rinsing & sealant tanks.DIRECTIONS FOR USE1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree ofsurface soil will determine the length of time and the number of cleaning steps and cleaningtemperature (M.S. Tank).2. Rinse thoroughly in overflowing cold water (M.S. Tank).3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at aconcentration of 1:1 at room temperature (FRP Tank).4. Rinse thoroughly in overflowing cold water (M.S. Tank).5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary toproduce the desired depth of black, is usually one to three minutes. For most parts a dilution ofone part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank).6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank). 7. Immerse the pieces in oil, a dewatering type rust preventive at room temperature for 3 minutesto seal the finish and impart corrosion resistance (M.S. Tank).The above parts can be sealed while wet or dry. If parts have to be dried prior to sealing, step 6should be followed with a hot water rinse and the parts to be sealed as soon as they are dry.A wide range of rust preventives are available with us. Consult us on what type of finish andprotection you require for your parts or components and we can suggest a suitable oil.

GENERAL DESCRIPTION. VCBLK HB-18 is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature.VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energysaving, fast, dependable and convenient. It increases productivity and lowers labour costs.Finishing can be done anywhere without special equipment, ventilation, heating systems or anycomplicated control procedures. EQUIPMENT REQUIREDAcid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used withVCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks andracks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used fordegreasing, rinsing & sealant tanks.DIRECTIONS FOR USE1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree ofsurface soil will determine the length of time and the number of cleaning steps and cleaningtemperature (M.S. Tank). 2. Rinse thoroughly in overflowing cold water (M.S. Tank). 3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at aconcentration of 1:1 at room temperature (FRP Tank). 4. Rinse thoroughly in overflowing cold water (M.S. Tank).5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary toproduce the desired depth of black, is usually one to three minutes. For most parts a dilution ofone part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank).6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank). 7. Immerse the pieces in oil, a dewatering type rust preventive at room temperature for 3 minutesto seal the finish and impart corrosion resistance (M.S. Tank).The above parts can be sealed while wet or dry. If parts have to be dried prior to sealing, step 6should be followed with a hot water rinse and the parts to be sealed as soon as they are dry.A wide range of rust preventives are available with us. Consult us on what type of finish andprotection you require for your parts or components and we can suggest a suitable oil.

We deal in Room Temperature blackening Chemical, which customer can directly avail from us. GENERAL DESCRIPTION VCBLK HB-18 is a new revolutionary development in cold black finishing. It will impart jet black conversion coating to steels, cast iron and other ferrous metals at room-temperature.VCBLK HB-18 process is easy to do in-house. It is non-caustic, non-splattering, safe, energysaving, fast, dependable and convenient. It increases productivity and lowers labour costs.Finishing can be done anywhere without special equipment, ventilation, heating systems or anycomplicated control procedures.EQUIPMENT REQUIREDAcid Resistant tanks, containers, tumbling barrels, baskets, hooks and racks must be used withVCBLK HB-18 and derusting tank. Plastic or Rubber lined tanks and plastic-coated hooks andracks are suitable for both VCBLK HB-18 and derusting tanks. Mild steel may be used fordegreasing, rinsing & sealant tanks.DIRECTIONS FOR USE1. Thoroughly clean and degrease the pieces to be blackened in KLN 18. The type and degree ofsurface soil will determine the length of time and the number of cleaning steps and cleaningtemperature (M.S. Tank).2. Rinse thoroughly in overflowing cold water (M.S. Tank).3. Surface rust, if present, should be removed following cleaning cycle using RLN 27 at aconcentration of 1:1 at room temperature (FRP Tank).4. Rinse thoroughly in overflowing cold water (M.S. Tank).5. Immerse the pieces in VCBLK HB-18 solution. VCBLK HB-18 solution is to be diluted with 6to 12 parts of water depending on alloy and surface, hardness. The immersion time necessary toproduce the desired depth of black, is usually one to three minutes. For most parts a dilution ofone part VCBLK HB-18 with 9 parts of water would give good results (FRP Tank).6. Rinse the pieces in overflowing cold water for 30 seconds (M.S. Tank). 7. Immerse the pieces in oil, a dewatering type rust preventive at room temperature for 3 minutesto seal the finish and impart corrosion resistance (M.S. Tank).The above parts can be sealed while wet or dry. If parts have to be dried prior to sealing, step 6should be followed with a hot water rinse and the parts to be sealed as soon as they are dry.A wide range of rust preventives are available with us. Consult us on what type of finish andprotection you require for your parts or components and we can suggest a suitable oil.

INTRODUCTION : CORONIL-555 is an antirust chemical compound that is readily soluble in water. It is widely used to give temporary protection against rusting of steel tubes, pipes, strips, profiles and various other ferrous parts, during process. CORONIL-555 is an antirust chemical compound that is readily soluble in water. USES : 1) It can be used as an anti-rust treatment after acid pickling or phosphating. The acid pickled or phosphated parts after rinsing are dipped or sprayed with the solution of CORONIL-555. 2) It can be used as a Passivation cum Neutralizer for machined components, for multi-metal assemblies, for ground parts and for various maintenance jobs after cleaning. It can be used either by dip, spray or by circulation. 3) It can be used as an antirust additive for : (a) Air-testing in water. (b) Hydro testing (especially of pipelines). 4) It can be added to cutting coolants or machining fluids to prevent rusting of cutting tools and workpieces for a few days.

1. ZNP-54 ZINC PHOSPHATING CHEMICAL 2. Generally zinc phosphate conversion coating is used to provide long lasting corrosion protection. Almost all automotive industries use this type of conversion coating. It is suitable for the products come against hard weather conditions. Coating quality is better than iron phosphate coating. It forms 2 - 5 gr/m² coating on the metal surface when used as under paint. Application, set up and control of this process are more difficult than other methods and can be applied by immersion or spray. 3. Organic compounds like nickel and manganese are added to the bath to increase the coating performance. Also activation can be used to form small phosphate crystals on the metal surface before zinc phosphating. 4. Zinc phosphate reaction happens in amorphous shape with gray - black color. 5. pH optimizers are added to accelerate the reaction. Temperature, application time, concentration, pH, total acid and free acid values are the parameters which must be under control. 6. Zinc phosphates, coating range between 7 - 15 gr/m², are used in wire drawing, tube drawing and cold forming industries. Phosphated metal workpieces are prepared to the next stage by application of protective lubricans and soap

DESCRIPTION : VCCLEAN-550 is a very effective deburring compound. It can also be used for cleaning, degreasing, derusting, descaling etc. when used in tumblers, vibrators, agitators and deburring equipments. It will remove all loose deposits producing a very smooth and even surface on the components. It can very safely be used for ferrous as well as non-ferrous metals. It is non-toxic and very safe to handle. USES : 1. For deburring ferrous & non-ferrous components. 2. For removal of rust & scales from components when used in tumblers & vibrators etc. alongwith some suitable media APPLICATION :- 1. Add 5-10% of VCCLEAN-550 based on the water added to the tank of the vibrator/tumbler etc. 2. Operate the equipment for a time ranging from ½ hr – 6 hrs depending on the type of operation. Regular addition of chemical may have ro be made for long duration of operation 3. Rinse tumble the components with fresh water. 4. Dip them in a suitable rust preventive like RUST PREVENTIVE OIL depending on the desired period of protection.

CHROMATIZING Aluminium chromate and its applications What we call as phosphating to steel an iron is called chromating for aluminium surfaces. Also it is knows as alodine coating. There are yellow, green and transparent chromating types. Yellow chromate coats Cr+6, green chromate coats Cr+3. Coating weight can vary according to application time and coating type. Drying temperature must not pass over 65 º C for yellow chromate and 85 º C for green and transparent chromate coatings. It is importat to provide clean, grease free surface before chromate application. If hot degreasing bath is prepared, caustic bath and following nitric acid bath can be used for pickling. On the other hand, acidic degreasing baths have pickling ability with itselves. Chromating and paint adhesion will be much better on pickled and degreased aluminium surface.